●特性及適用范圍:

是性能良好(hao)的(de)(de)(de)滲(shen)碳(tan)鋼，淬(cui)(cui)透性較(jiao)高(gao)(gao)，經滲(shen)碳(tan)淬(cui)(cui)火后(hou)具(ju)有(you)硬而耐磨的(de)(de)(de)表面(mian)與堅韌的(de)(de)(de)心部，具(ju)有(you)較(jiao)高(gao)(gao)的(de)(de)(de)低溫沖(chong)(chong)(chong)擊(ji)韌性，焊接性中(zhong)(zhong)等(deng)，正火后(hou)可切削性良好(hao)。用(yong)(yong)(yong)(yong)于(yu)制(zhi)造截面(mian)<30mm的(de)(de)(de)承(cheng)受(shou)高(gao)(gao)速、中(zhong)(zhong)等(deng)或重載荷、沖(chong)(chong)(chong)擊(ji)及摩(mo)擦(ca)(ca)的(de)(de)(de)重要零(ling)件，如(ru)齒(chi)輪(lun)、齒(chi)圈(quan)、齒(chi)輪(lun)軸(zhou)十字(zi)頭(tou)等(deng)。是18CrMnTi的(de)(de)(de)代用(yong)(yong)(yong)(yong)鋼，廣泛用(yong)(yong)(yong)(yong)作滲(shen)碳(tan)零(ling)件，在汽車.拖拉(la)機工(gong)業用(yong)(yong)(yong)(yong)于(yu)截面(mian)在30mm以下，承(cheng)受(shou)高(gao)(gao)速.中(zhong)(zhong)或重負荷以及受(shou)沖(chong)(chong)(chong)擊(ji).摩(mo)擦(ca)(ca)的(de)(de)(de)重要滲(shen)碳(tan)零(ling)件，如(ru)齒(chi)輪(lun).軸(zhou).齒(chi)圈(quan).齒(chi)輪(lun)軸(zhou).滑動軸(zhou)承(cheng)的(de)(de)(de)主軸(zhou).十字(zi)頭(tou).爪形(xing)離合器.蝸桿等(deng)。

       碳C:0.17~0.23

硅Si:0.17~0.375120

錳(meng)Mn:0.80~1.10

鉻Cr:1.00~1.30

硫S: 優(you)質鋼不(bu)大于0.030

高級優質鋼不大于0.020

特(te)級(ji)優質鋼不大于0.010

磷(lin)P: 優質鋼不大(da)于0.030

高級優質鋼(gang)不大于0.020

特(te)級(ji)優質鋼不大于0.020

鎳Ni:優質鋼不大于(yu)0.30

高級優質鋼不大(da)于0.30

特級優質鋼不大于0.30

銅(tong)Cu(注(zhu)1):優質鋼不大于(yu)0.30

高級(ji)優質鋼不大于0.25

特級優質鋼不大(da)于0.25

鈦Ti:0.04~0.10

注1:熱(re)壓力加工(gong)用鋼(gang)的銅含量不(bu)大于0.2%

力學性能

●力學性能:5120

抗拉強度(du)σb (MPa):≥1080(110)

屈(qu)服(fu)強度σs (MPa):≥835(85)

伸長率δ5 (%):≥10

斷面收縮率ψ (%):≥45

沖擊功Akv (J):≥55

沖擊韌性值αkv (J/cm2):≥69(7)

硬度:≤217HB

試樣(yang)尺寸:試樣(yang)毛坯(pi)尺寸為15mm

●5120密度:7.8×10kg/m3

彈性模量(liang):207GPa

泊松比:0.25

導熱率:1.26×10-5(1/℃)